Experimental study of natural hydroxyapatite/chitosan composite on reconstructing bone defects
Author:
Affiliation:

Fund Project:

This study was supported by Science and Technology Projects Fund of Nanjing Medical University(NY0522)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    Abstract:

    Objective:To study the possibility of natural hydroxyapatite/chitosan composite on repairing bone defects. Methods:We developed a natural hydroxyapatite/chitosan composite that could be molded into any desired shape. The powder component consists of natural hydroxyapatite, which is epurated from bone of pigs. The liquid component consists of malic acid and chitosan. Operations were performed on the left tibias of 15 white rabbits to create two square bone defects. One of the defects was reconstructed with the composite, while the other was not repaired and used as a blank control. Three of the animals were killed at the end of 2 weeks, 4 weeks, 8 weeks, 12 weeks and 16 weeks respectively and implants were evaluated anatomically and histologically. Results:No apparent rejection reaction was found, except for a mild inflammatory infiltration observed 2 weeks after surgery. Fibrous tissue became thinner 2 ~8 weeks after surgery and bony connections were detected 12 weeks after surgery. The new bone was the same as the recipient bone by the 16th postoperative week. Conclusion:The hydroxyapatite/chitosan composite has good biocompatibility and osteoconduction. It is a potential repairing material for clinical application.

    参考文献
    相似文献
    引证文献
引用本文

Hua Yuan, Ning Chen, Xiaoying Lv, Buzhong Zheng.[J].南京医科大学学报(自然科学版),2008,28(6):372-375

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2008-07-26
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期:
通知关闭
郑重声明